AISI Aprox. W1
Breve descripción:
Designation by Standards Mat. No. DIN EN AISI - - - Approx. W1 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.81 0.20 0.40 - - - - - - Description This alloy is one of the common water hardening tool steel grades available. W1 is basically a simple high carbon steel and is easily hardened by heating and quenching in water, just as with plain carbon steel alloys. The W series of tool steels are a very simple alloy group, low ...
Detalle del producto
Preguntas más frecuentes
Etiquetas de productos
Designación por las Normas
| Estera. No. | ESTRUENDO | ES | AISI |
| - | - | - | Aprox. W1 |
Composición química (en% en peso)
| do | Si | Minnesota | cr | Mes | Ni | V | W | Otros |
| 0,81 | 0.20 | 0.40 | - | - | - | - | - | - |
Descripción
This alloy is one of the common water hardening tool steel grades available. W1 is basically a simple high carbon steel and is easily hardened by heating and quenching in water, just as with plain carbon steel alloys. The W series of tool steels are a very simple alloy group, low cost, and responsive to simple heating and water quenching for hardening. The alloy does undergo considerable distortion during quenching.Las solicitudes
W1 is commonly used for hand operated metal cutting tools, cold heading, embossing taps and reamers as well as cutlery.Las propiedades físicas (valores avarage) a temperatura ambiente
Módulo de elasticidad [10 3 x N / mm 2]: 210
Densidad [g / cm 3]: 7.87
Thermal conductivity [W/m.K]: 46.0
Electric resistivity [Ohm mm2/ m] : 0,17
Specific heat capacity[J/g.K]: 0.46Coeficiente de expansión térmica lineal 10 -6 o do-1
| 20-100 o do | 20-200 o do | 20-300 o do | 20-400 o do | 20-500 o do |
| 11.1 | 12.1 | 12.9 | 13.5 | 13.9 |
Transformación por enfriamiento continuo (CCT) Diagrama
El recocido suave
Heat to 680-720o C, enfriar lentamente en el horno. Esto producirá una dureza máxima Brinell de 192.El Estrés
Stress relieving to remove machining stresses should be carried out by heating to approx. 600-650o C, manteniendo durante 1-2 horas a calor, seguido por enfriamiento al aire. Esta operación se realiza para reducir la distorsión durante el tratamiento térmico.Endurecimiento
Harden from a temperature of 780-810o C seguido de agua. Dureza después del temple es 64 HRC.Templado
Tempering temperature: See the data bellow.La temperatura de revenido ( o C) vs. Dureza (HRC)
| 100o do | 200o do | 300o do | 400o do | 450o do |
| 67 | 64 | 54.5 | 45.5 | 42 |
Diagrama de revenido
La forja
Hot forming temperature: 1050-800o C.Maquinabilidad
W1 is a plain carbon steel and machines with ease. It is the base line of 100% machinability on which machinability of the other tool steels is compared.Resistencia a la corrosión
This is a plain carbon steel and it will corrode unless protected.Soldadura
W1 may be welded by all of the standard techniques.Exención de responsabilidad
La información y los datos presentados en este documento son valores típicos o promedio y no son una garantía de los valores máximos o mínimos. Las aplicaciones sugeridas específicamente para el material descrito en este documento se hacen únicamente con el propósito de ilustración para permitir que el lector haga su propia evaluación y no pretenden ser garantía, ya sea expresa o implícita, de idoneidad para estos u otros puposes. No hay ninguna declaración de que el destinatario de esta literatura recibirá ediciones actualizadas como estén disponibles.