Mat.No. 1.2510, DIN 100MnCrW4, O1
Breve descripción:
Designation by Standards Mat. No. DIN EN AISI 1.2510 100MnCrW4 95MnWCr5 O1 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.95 0.25 1.20 0.48 - - 0.13 0.55 - Description This alloy is one of the cold work, oil hardening type tool steels. It is relatively inexpensive containing small amounts of manganese, tungsten and chromium. Hardening by oil quench minimizes distortion and cracking. Applications Applications include short ru...
Detalle del producto
Preguntas más frecuentes
Etiquetas de productos
Designación por las Normas
| Estera. No. | ESTRUENDO | ES | AISI |
| 1.2510 | 100MnCrW4 | 95MnWCr5 | O1 |
Composición química (en% en peso)
| do | Si | Minnesota | cr | Mes | Ni | V | W | Otros |
| 0.95 | 0.25 | 1.20 | 0.48 | - | - | 0.13 | 0.55 | - |
Descripción
This alloy is one of the cold work, oil hardening type tool steels. It is relatively inexpensive containing small amounts of manganese, tungsten and chromium. Hardening by oil quench minimizes distortion and cracking.Las solicitudes
Applications include short run tooling for blanking dies, cold forming dies and cutting tools operating at ambient temperature. For working tools, cutting blades, sizing and stamping tools.Las propiedades físicas (valores avarage) a temperatura ambiente
Densidad [g / cm 3]: 7,85
Thermal conductivity [W/m.K]: 30.0Coeficiente de expansión térmica lineal 10 -6 o do-1
| 20-100 o do | 20-200 o do | 20-300 o do | 20-400 o do | 20-500 o do | 20-600 o do | 20-700 o do |
| 12.1 | 12.9 | 13.3 | 14.0 | 14.4 | 14.8 | 14.9 |
Transformación por enfriamiento continuo (CCT) Diagrama
El recocido suave
Heat to 740-770o C, enfriar lentamente en el horno. Esto producirá una dureza máxima Brinell de 230.Endurecimiento
Harden from a temperature of 780-820o C seguido de aceite, baño caliente (180-220 o C) de temple. Dureza después del temple es 64 HRC.Templado
Tempering temperature: See the data bellow.La temperatura de revenido ( o C) vs. Dureza (HRC)
| 100o do | 200o do | 300o do | 400o do | 500o do | 600o do | 650o do |
| 64 | 61 | 56 | 51 | 44 | 37 | 34 |
Diagrama de revenido
La forja
Hot forming temperature: 1037-875o C.Maquinabilidad
Machinability of this alloy is very good. It has a rating of 90% that of the W group water hardening low alloy tool steels.Resistencia a la corrosión
This is a relatively simple steel alloy and does not resist ordinary corrosion. It will rust unless protected.Soldadura
This alloy is weldable by standard means. Consult the alloy supplier for details and procedures.Exención de responsabilidad
La información y los datos presentados en este documento son valores típicos o promedio y no son una garantía de los valores máximos o mínimos. Las aplicaciones sugeridas específicamente para el material descrito en este documento se hacen únicamente con el propósito de ilustración para permitir que el lector haga su propia evaluación y no pretenden ser garantía, ya sea expresa o implícita, de idoneidad para estos u otros puposes. No hay ninguna declaración de que el destinatario de esta literatura recibirá ediciones actualizadas como estén disponibles.