Mat.No. 1.1121, DIN CK10, AISI 1010
Designation by Standards Mat. No. DIN EN AISI 1.1121 Ck10 - 1010 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.10 max. 0.40 0.45 - - - - - - Description CK10 is a plain carbon steel with a nominal 0.10% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased strength. Applications The low carbon steels, such as CK10, are used for applications such as cold headed fasteners and ...
Detalle del producto
Preguntas más frecuentes
Etiquetas de productos
Designación por las Normas
Composición química (en% en peso)
Descripción CK10 is a plain carbon steel with a nominal 0.10% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased strength. Las solicitudes The low carbon steels, such as CK10, are used for applications such as cold headed fasteners and bolts. Las propiedades físicas (valores avarage) a temperatura ambiente Modulus of elasticity [103 x N / mm 2]: 210 Density [g/cm3]: 7.85 El recocido suave Heat to 800-840o C, cool slowly. Endurecimiento This steel is generally used in the annealed or case hardened condition. It may be heat treated, quenched and tempered but the cost for so doing is generally not worth the result. Templado Tempering temperature: 320-530o C.La forja Hot forming temperature: 1050-850o C.Maquinabilidad Machinability of CK10 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AISI 1112 as a reference that is considered 100% machinable (easily machined) the CK10 steel has a rating of 55%. Resistencia a la corrosión This is a plain carbon steel and has no corrosion resistance. It will rust unless protected. Soldadura CK10 steel may be welded by all of the standard welding techniques. Trabajo en frío CK10 is easily cold worked by traditional means. Following severe cold working a stress relief, or full, anneal should be performed. Exención de responsabilidad The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.