Mat.No. 1.0605, DIN C75, AISI 1075

Breve descripción:

Designation by Standards Mat. No. DIN EN AISI 1.0605 C75 - 1075 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.75 0.25 0.70 - - - - - - Description This is one of the higher carbon steels used for high hardness in the fully hardened condition. In such condition the steel is more brittle than the lower carbon steels. Applications Applications include springs and cutting tools. Physical properties (avarage values) at ambient t...

Precio FOB: US $ 0.5 - 9.999 / pieza

Min.Order Cantidad: 100 pedazos / pedazos

Capacidad de la fuente: 10000 pedazos / pedazos por mes

Puerto: Shenzhen

Condiciones de pago: L / C, D / A, D / P, T / T

Enviar correo electrónico a nosotros Descargar como PDF

Detalle del producto

Preguntas más frecuentes

Etiquetas de productos

Designación por las Normas

Estera. No.	ESTRUENDO	ES	AISI
1,0605	C75	-	1075

Composición química (en% en peso)

do	Si	Minnesota	cr	Mes	Ni	V	W	Otros
0.75	0.25	0.70	-	-	-	-	-	-

Descripción
This is one of the higher carbon steels used for high hardness in the fully hardened condition. In such condition the steel is more brittle than the lower carbon steels.

Las solicitudes
Applications include springs and cutting tools.

Las propiedades físicas (valores avarage) a temperatura ambiente
Módulo de elasticidad [10 ³ x N / mm ²]: 210
Densidad [g / cm ³]: 7,85

El recocido suave
Heat to 925^oC, enfriar lentamente.

Endurecimiento
Harden from a temperature of 890^oC seguido de temple en aceite.

Templado
Tempering temperature: Please ask

La forja
caliente temperatura de formación: 1100-850 ^oC.

Maquinabilidad
The machinability of this steel suffers because of the high carbon content. It rates at 50% that of the AISI 1112 steel that is considered the 100% machinable base reference.

Resistencia a la corrosión
This is a steel and will rust unless protected. It is not a corrosion resistant alloy.

Soldadura
C75 is weldable by all of the welding techniques. However it is important to use pre-heat and post-heat practice as given in approved weld procedure, in order to avoid cracking. Pre-heat at 260 to 320^oC y post-térmico a 650 a 780 ^oC.

Trabajo en frío
Cold working of C75 is difficult even in the annealed condition. However it may be done by conventional methods but requires more force than for the low carbon steels.

Exención de responsabilidad
La información y los datos presentados en este documento son valores típicos o promedio y no son una garantía de los valores máximos o mínimos. Las aplicaciones sugeridas específicamente para el material descrito en este documento se hacen únicamente con el propósito de ilustración para permitir que el lector haga su propia evaluación y no pretenden ser garantía, ya sea expresa o implícita, de idoneidad para estos u otros puposes. No hay ninguna declaración de que el destinatario de esta literatura recibirá ediciones actualizadas como estén disponibles.