Mat.No. 1.1221، DIN Ck60، ايسي 1060
وصف قصير:
Designation by Standards Mat. No. DIN EN AISI 1.1221 Ck60 - 1060 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.61 max. 0.40 0.75 max. 0.40 max. 0.10 max. 0.40 - - (Cr+Mo+Ni) = max. 0.63 Description CK60 is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades. Applications Shafts, bushings, connecting rods, nechanical engineering components, agricultural hand tools, large forgings, springs, cold rolle...
تفاصيل المنتج
التعليمات
علامات المنتج
تسمية المعايير
حصيرة. لا. DIN EN ايسي 1.1221 Ck60 - 1060 التركيب الكيميائي (وزن٪)
C سي مليون كر مو ني الخامس W الآخرين 0.61 كحد أقصى. 0.40 0.75 كحد أقصى. 0.40 كحد أقصى. 0.10 كحد أقصى. 0.40 - - (الكروم + مو + ني) = كحد أقصى. 0.63 وصف CK60 is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades. تطبيقات Shafts, bushings, connecting rods, nechanical engineering components, agricultural hand tools, large forgings, springs, cold rolled strips. الخصائص الفيزيائية (قيم أفاراجي) في درجة حرارة الجو المحيط Modulus of elasticity [103 س N / مم 2]: 210 Density [g/cm3]: 7.85 لينة التليين Heat to 650-700س C, cool slowly in furnace. This will produce a maximum Brinell hardness of 241. تطبيع Normalizing temperature: 820-850س C.تصلب Harden from a temperature of 800-830س C، 810-840 س C followed by water or oil quenching. هدأ Tempering temperature: 540-680س C.هدأ مخطط
Click the image to enlarge the diagram. خصائص الميكانيكية في تطبيع الحالة
القطر (مم) 0.2٪ الإجهاد الإثبات (N / مم 2) قوة الشد (N / مم 2) استطالة (٪) ما يصل الى 16 380 710 10 17-40 340 670 11 41-100 340 670 11 101-160 310 650 11 161-250 310 650 11 خصائص الميكانيكية في المسقي والحالة
القطر (مم) 0.2٪ الإجهاد الإثبات (N / مم 2) قوة الشد (N / مم 2) استطالة (٪) اختزال (٪) قوة تأثير (J) ما يصل الى 16 580 850-1000 11 25 - 17-40 520 800-950 13 30 - 41-100 450 750-900 14 35 - 101-160 - - - - - 161-250 - - - - - التصلب مخطط
Click the image to enlarge the diagram. تزوير Hot forming temperature: 1100-850س C.التشغيل في الماكينات Machinability of CK60 and all of the higher carbon steels is relatively poor. CK60 rates at 55 to 60 % that of the AISI 1112 steel which is considered 100% machinable. المقاومة للتآكل This steel is not corrosion resistant. it will rust unless protected. لحام CK60 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260س C وبعد الحرارة في 590-650 س C practice per an approved welding procedure. العمل الباردة Cold working is difficult even in the annealed condition although it may be done by conventional methods but requires greater force than the lower carbon steels. Forms manufactured: Please see the Dimensional Sales Program. تنصل The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available. Unless otherwise specified, registered trademarks are property of Metal Ravne company. Copyright 2015 by Metal Ravne. All rights reserved. Contact our Sales Office for more information.