AISI 1006 Carbon Steel

AISI 1006 Carbon Steel

Short Description:

Chemical Composition The following table shows the chemical composition of AISI 1006 carbon steel. Element Content (%) Iron, Fe 99.43-99.75 Manganese, Mn 0.25-0.40 Carbon, C 0.080 Sulfur, S 0.050 Phosphorous, P 0.040 Physical Properties The physical properties of AISI 1006 carbon steel are outlined in the following table. Properties Metric Imperial Density 7.872 g/cm3 0.2844 lb/in³ Mechanical Properties The mechanical properties of AISI 1006 cold drawn carbon steel are...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    FAQ

    Product Tags

    Chemical Composition

    The following table shows the chemical composition of AISI 1006 carbon steel.

    Element Content (%)
    Iron, Fe 99.43-99.75
    Manganese, Mn 0.25-0.40
    Carbon, C 0.080
    Sulfur, S 0.050
    Phosphorous, P 0.040

    Physical Properties

    The physical properties of AISI 1006 carbon steel are outlined in the following table.

    Properties Metric Imperial
    Density 7.872 g/cm3 0.2844 lb/in³

    Mechanical Properties

    The mechanical properties of AISI 1006 cold drawn carbon steel are tabulated below.

    Properties Metric Imperial
    Tensile strength 330 MPa 47900 psi
    Yield strength (depending on temper) 285 MPa 41300 psi
    Elastic modulus 190-210 GPa 27557-30458 ksi
    Bulk modulus (typical for steel) 140 GPa 20300 ksi
    Shear modulus (typical for steel) 80.0 GPa 11600 ksi
    Poisson’s ratio 0.27-0.30 0.27-0.30
    Elongation at break (in 50 mm) 20% 20%
    Reduction of area 45% 45%
    Hardness, Brinell 95 95
    Hardness, Knoop (converted from Brinell hardness) 113 113
    Hardness, Rockwell B (converted from Brinell hardness) 55 55
    Hardness, Vickers (converted from Brinell hardness) 98 98
    Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing) 50 50

    Thermal Properties

    The thermal properties of AISI 1006 carbon steel are tabulated below.

    Properties Metric Imperial
    Thermal expansion co-efficient (@0.000-100°C/32-212°F) 12.6 µm/m°C 7 µin/in°F

    Other Designations

    Equivalent materials to AISI 1006 carbon steel are:

    • AMS 5041
    • ASME 5041
    • ASTM A29
    • ASTM A510
    • ASTM A545
    • FED QQ-W-461
    • MIL SPEC MIL-S-11310 (CS1006)
    • SAE J403
    • SAE J412 (1005)
    • SAE J414

    Applications

    AISI 1006 carbon steel is primarily used in applications which require hard bending and welding such as panels for appliances or automobiles. AISI 1006 carbon steel can also be used in magnet core applications.

     