Mat.No. 1.1240, DIN 65Mn4

Mat.No. 1.1240, DIN 65Mn4

Short Description:

Designation by Standards Mat. No. DIN EN AISI 1.1240 65Mn4 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.65 0.38 1.05 0.13 - - - - - Description Unalloyed carbon steel. Applications Special purpose steel.  Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.85 Soft Annealing Brinell hardness in annealed condition is max. 245. Normalizing Please ask. Stress Relieving Stress relieving to r...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    FAQ

    Product Tags

    Designation by Standards

    Mat. No. DIN EN AISI
    1.1240 65Mn4 - -

    Chemical Composition (in weight %)

    C Si Mn Cr Mo Ni V W Others
    0.65 0.38 1.05 0.13 - - - - -

    Description Unalloyed carbon steel. Applications Special purpose steel.  Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.85 Soft Annealing Brinell hardness in annealed condition is max. 245. Normalizing Please ask. Stress Relieving Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment. Hardening Please ask. Tempering Tempering temperature: Please ask. Forging Hot forming temperature: Please ask.  Machinability Please ask. Disclaimer The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.