Mat.No. 1,1193, DIN CF45, AISI 1045
Designation by Standards Mat. No. DIN EN AISI 1.1193 CF45 - 1045 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.46 0.25 0.65 - - - - - - Description CF45 is a medium carbon steel is used when greater strength and hardness is desired than in the “as rolled” condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned, ground and polished. Applications...
Информация о продукте
Обозначение по стандартам
Химический состав (в весовых%)
Описание CF45 is a medium carbon steel is used when greater strength and hardness is desired than in the “as rolled” condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned, ground and polished. Применение Used in gears, shafts, axles, bolts, studs, and machine parts. Физические свойства (значения) курсы , при температуре окружающей среды Modulus of elasticity [103 х Н / мм 2]: 210 Density [g/cm3]: 7.85 Мягкий Отжиг Heat to 650-700O C, cool slowly. This will produce a maximum Brinell hardness of 207. Нормализация Temperature: 840-870O С.Снятия напряжения Stress relieving to remove machining stresses should be carried out by heating to 120-200O C, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment. Закалка Harden from a temperature of 820-850O C followed by oil or water quenching. Hardness after quenching is 55-61 HRC. Закалка Tempering temperature: 550-660O С.Ковка Hot forming temperature: 1100-850O С.Machinability No data. Отказ от ответственности The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.