Mat.No. 1.1140, DIN Cm15, AISI 1015
Short Description:
Designation by Standards Mat. No. DIN EN AISI 1.1140 Cm15 - 1015 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.15 max.0.40 0.45 - - - - - S=0.020-0.040% Description CM15 is a plain carbon steel with a nominal 0.15% carbon content and higher content of S (0.020-0.040%). Applications Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Steels for case hardening. Physi...
Product Detail
FAQ
Product Tags
Designation by Standards
Mat. No. | DIN | EN | AISI |
1.1140 | Cm15 | - | 1015 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.15 | max.0.40 | 0.45 | - | - | - | - | - | S=0.020-0.040% |
Description
CM15 is a plain carbon steel with a nominal 0.15% carbon content and higher content of S (0.020-0.040%).Applications
Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Steels for case hardening.Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85Soft Annealing
Heat to 650-700oC, cool slowly in furnace.Carburizing
Carburizing temperature: 880-980oC.
Cooling from carburizing temperature: water, oil, air, thermal bath.
Core hardening temperature: 880-920oC.Tempering
Tempering temperature: 150-180oC.Forging
Hot forming temperature: 1050-850oC.Machinability
Machinability of CM15 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AISI 1112 as a reference that is considered 100% machinable (easily machined) the CM15 steel has a rating of 55%.Forms manufactured: Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.Unless otherwise specified, registered trademarks are property of Metal Ravne company. Copyright 2015 by Metal Ravne. All rights reserved. Contact our Sales Office for more information.