Mat.No. 1.1223, DIN Cm60, AISI 1060

Mat.No. 1.1223, DIN Cm60, AISI 1060

Short Description:

  Designation by Standards   Mat. No. DIN EN AISI 1.1223 Cm60 - 1060   Chemical Composition (in weight %)   C Si Mn Cr Mo Ni V W Others 0.61 max. 0.40 0.75 max. 0.40 max. 0.10 max. 0.40 - - (Cr+Mo+Ni) = max. 0.63   Description CM60 is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades. Applications Shafts, bushings, connecting rods, nechanical engineering components, agricultural hand tools, ...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    FAQ

    Product Tags

     

    Designation by Standards

     

    Mat. No. DIN EN AISI
    1.1223 Cm60 - 1060

     

    Chemical Composition (in weight %)

     

    C Si Mn Cr Mo Ni V W Others
    0.61 max. 0.40 0.75 max. 0.40 max. 0.10 max. 0.40 - - (Cr+Mo+Ni) = max. 0.63

     

    Description CM60 is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades. Applications Shafts, bushings, connecting rods, nechanical engineering components, agricultural hand tools, large forgings, springs, cold rolled strips. Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.85 Soft Annealing Heat to 650-700oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 241. Normalizing Normalizing temperature: 820-850oC. Hardening Harden from a temperature of 800-830oC, 810-840oC followed by water or oil quenching. Tempering Tempering temperature: 540-680oC. Forging Hot forming temperature: 1100-850oC. Machinability Machinability of CM60 and all of the higher carbon steels is relatively poor. CM60 rates at 55 to 60 % that of the AISI 1112 steel which is considered 100% machinable. Corrosion Resistance This steel is not corrosion resistant. it will rust unless protected. Welding CM60 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260oC and post-heat at 590 to 650oC practice per an approved welding procedure. Cold working Cold working is difficult even in the annealed condition although it may be done by conventional methods but requires greater force than the lower carbon steels. Forms manufactured: Please see the Dimensional Sales Program. Disclaimer The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available. Unless otherwise specified, registered trademarks are property of Metal Ravne company. Copyright 2015 by Metal Ravne. All rights reserved. Contact our Sales Office for more information.

     