Mat.No. 1.7711, DIN 40CrMoV4-7
Designation by Standards Brand Name Ravne No. Mat. No. DIN EN AISI PO210 210 1.7711 40CrMoV4-7 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.40 0.25 0.58 1.05 0.68 - 0.30 - - DescriptionAlloyed carbon steel. ApplicationsStaticaly and dymamicaly stressed components for vehicles, engines and machines, for parts of lager cross sections, gears, crankshafts. Hardness as surface hardened is more than 54 HRC. Physical properties (avarage values) at ambien...
Designation by Standards
|Brand Name||Ravne No.||Mat. No.||DIN||EN||AISI|
Chemical Composition (in weight %)
Alloyed carbon steel.
Staticaly and dymamicaly stressed components for vehicles, engines and machines, for parts of lager cross sections, gears, crankshafts. Hardness as surface hardened is more than 54 HRC.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Heat to 650-730oC, cool slowly. This will produce a maximum Brinell hardness of 241.
Harden from a temperature of 880-930oC followed by oil or water (conditional) quenching.
Tempering temperature: 670-730oC.
Hot forming temperature: 1100-850oC.
Forms manufactured: Please see theDimensional Sales Program.
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.