Mat.No. 1.7380, DIN 10CrMo9-10, AISI A182 Grade F22
Designation by Standards Brand Name Ravne No. Mat. No. DIN EN AISI PT181 181 1.7380 10CrMo9-10 - A182 Grade F22 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.12 max. 0.40 0.55 2.25 1.00 max. 0.50 - - - DescriptionThis is chromium-molybdenum structural steel. ApplicationsComponent parts for steam boilers and turbines, shafts for higher temperature ranges.Physical properties (avarage values) at ambient temperatureModulus of elasticity [103 x N/mm2]: 190-2...
Designation by Standards
|Brand Name||Ravne No.||Mat. No.||DIN||EN||AISI|
|PT181||181||1.7380||10CrMo9-10||-||A182 Grade F22|
Chemical Composition (in weight %)
|0.12||max. 0.40||0.55||2.25||1.00||max. 0.50||-||-||-|
This is chromium-molybdenum structural steel.
Component parts for steam boilers and turbines, shafts for higher temperature ranges.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 190-210
Density [g/cm3]: 7.80
Stress relieving to remove machining stresses should be carried out by heating to 675oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Tempering temperature: 650-750oC.
Hot forming temperature: 1050-850oC.
Forms manufactured: Please see the Dimensional Sales Program.
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.