Mat.No. 1.2826, DIN 60MnSiCr4
Designation by Standards Brand Name Ravne No. Mat. No. DIN EN AISI VZ197 197 1.2826 60MnSiCr4 - - Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.62 0.90 1.00 0.30 - - - - - DescriptionVZ197 is a heat treatable, low alloy steel containing manganese, silicon and chromium. ApplicationsDies and lower dies, tri mming tools, hammer and pressing saddles. Physical properties (avarage values) at ambient temperatureModulus of elasticity [103 x N/mm2]: ...
Designation by Standards
|Brand Name||Ravne No.||Mat. No.||DIN||EN||AISI|
Chemical Composition (in weight %)
VZ197 is a heat treatable, low alloy steel containing manganese, silicon and chromium.
Dies and lower dies, tri mming tools, hammer and pressing saddles.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.78
Continuous Cooling Transformation (CCT) Diagram
Click the image to enlarge the diagram.
Heat to 680-720oC, cool slowly. This will produce a maximum Brinell hardness of 240.
Harden from a temperature of 820-860oC followed by oil quenching or hot quenching at 180-220oC.
Tempering temperature: 300-550oC.
Hot forming temperature: 1050-850oC.
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
This is a low alloy steel and not a corrosion resistant alloy. Protective coating should be used.
The alloy can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.
Forms manufactured: Please see the Dimensional Sales Program.
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.