Mat.No. 1.2344, DIN X40CrMoV51, AISI H13

Mat.No. 1.2344, DIN X40CrMoV51, AISI H13

Short Description:

Designation by Standards Mat. No. DIN EN AISI 1.2344 X40CrMoV51 X40CrMoV51 H13 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.39 1.00 0.38 5.15 1.35 - 1.00 - - Description This alloy is one of the hot work, chromium type tool steels. It also contains molybdenum and vanadium as strengthening agents. The chromium content assists this alloy to resist softening if used at higher temperatures. Secondary hardening steels with good tempering reistance. It maintains ...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    FAQ

    Product Tags

    Designation by Standards

    Mat. No. DIN EN AISI
    1.2344 X40CrMoV51 X40CrMoV51 H13

    Chemical Composition (in weight %)

    C Si Mn Cr Mo Ni V W Others
    0.39 1.00 0.38 5.15 1.35 - 1.00 - -

    Description
    This alloy is one of the hot work, chromium type tool steels. It also contains molybdenum and vanadium as strengthening agents. The chromium content assists this alloy to resist softening if used at higher temperatures. Secondary hardening steels with good tempering reistance. It maintains high hardness and strength at elevated temperatures. Good resistance to thermal fatigue, erosion and wear. Steel with very high thoughness and good ductilityand hardenability. Tools can be water cooled. 

    Applications
    H13 finds applications for hot die work, die casting and extrusion dies, wear resisting tools, pressure die casting tools, pressing tools for light and heavy metal. For the highest requirements we recommended UTOPMO2 ESR EFS. 

    Physical properties (avarage values) at ambient temperature
    Modulus of elasticity [103 x N/mm2]: 215 
    Density [g/cm3]: 7.78
    Thermal conductivity [W/m.K]: 25.0 
    Electric resistivity [Ohm mm2/m]: 0.52
    Specific heat capacity[J/g.K]: 0.46

    Thermal conductivity [W/m.K]M

    20oC 500oC 600oC
    25 28.5 29.3

    Density [g/cm3]

    20oC 500oC 600oC
    7.78 7.64 7.60

    Electric resistivity [Ohm mm2/m]

    20oC 500oC 600oC
    0.52 0.86 0.96

    Specific heat capacity[J/g.K]

    20oC 500oC 600oC
    0.46 0.55 0.59

    Coefficient of Linear Thermal Expansion 10-6 oC-1

    20-100oC 20-200oC 20-300oC 20-400oC 20-500oC 20-600oC 20-700oC 20-800oC
    10.7 11.9 12.2 12.5 12.7 13.1 13.5 13.7

    Continuous Cooling Transformation (CCT) Diagram


    Click the image to enlarge the diagram.

    Soft Annealing
    Heat to 760-810oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.

    Hardening
    Harden from a temperature of 1020-1060oC followed by oil, air quenching or warm bath (450-550oC). Hardness after quenching is 52-56 HRC.

    Tempering
    Tempering temperature: See the diagram bellow.

    Tempering Temperature (oC) vs. Hardness (HRC) vs. Tensile Stregth (N/mm2)

    100oC 200oC 300oC 400oC 500oC 550oC 600oC 650oC 700oC
    53 52 51 52 54 53 50 43 31
    1845 1790 1730 1790 1910 1845 1680 1360 995

    Tempering Diagram


    Click the image to enlarge the diagram.

    Diagram Tempering Temperature – Mechanical Properties


    Click the image to enlarge the diagram.

    Forging
    Hot forming temperature: 1100-900oC. 

    Machinability
    Machinability of H13 is medium to good. It rates as 75 % that of the W group water hardening tool steels which are low alloy and of generally good machinability.

    Corrosion Resistance 
    This alloy has some corrosion resistance due to its chromium content. However it is still a steel and will rust unless given protective coating.

    Welding 
    This alloy is weldable. Contact the alloy supplier for information on welding procedures.

    Forms manufactured: Please see the  Dimensional Sales Program. 

    Disclaimer
    The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.