Short Description:

  Designation by Standards   Mat. No. DIN EN AISI 1.3539 100CrMnMo8 - -   Chemical Composition (in weight %)   C Si Mn Cr Mo Ni V W Others 0.97 0.50 0.95 1.93 0.55 - - - -   Description Low alloyed cold working tool steel with Mn, Cr and Mo. Applications Through-hardenable. Roller bearings. Physical properties (avarage values) at ambient temperature Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.80 Soft Annealing Heat to approx. 750oC, coo...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Port: Shenzhen
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    FAQ

    Product Tags

     

    Designation by Standards

     

    Mat. No. DIN EN AISI
    1.3539 100CrMnMo8 - -

     

    Chemical Composition (in weight %)

     

    C Si Mn Cr Mo Ni V W Others
    0.97 0.50 0.95 1.93 0.55 - - - -

     

    Description
    Low alloyed cold working tool steel with Mn, Cr and Mo.

    Applications
    Through-hardenable. Roller bearings.

    Physical properties (avarage values) at ambient temperature
    Modulus of elasticity [103 x N/mm2]: 210
    Density [g/cm3]: 7.80

    Soft Annealing
    Heat to approx. 750oC, cool slowly. This will produce a maximum Brinell hardness of 217.

    Hardening
    Harden from a temperature of 800-850oC followed by oil quenching. Hardness after quenching is approx. 59 HRC.

    Tempering
    Tempering temperature: 100-250oC.

    Forging
    Hot forming temperature: 1050-850oC.

    Machinability
    No data.

    Disclaimer
    The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.