Mat.No. 1.6580, DIN 30CrNiMo8, AISI 4340

Mat.No. 1.6580, DIN 30CrNiMo8, AISI 4340

Short Description:

Designation by Standards Brand Name Ravne No. Mat. No. DIN EN AISI VCNMO200 750 1.6580 30CrNiMo8 30CrNiMo8 4340 Chemical Composition (in weight %) C Si Mn Cr Mo Ni V W Others 0.30 max. 0.40 0.45 2.00 0.40 1.90 - - - DescriptionVCNMO200 is a heat treatable, low alloy steel containing nickel, chromium and molybdenum. It is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength.  ApplicationsFor ...


Product Detail

FAQ

Product Tags

Designation by Standards

Brand Name Ravne No. Mat. No. DIN EN AISI
VCNMO200 750 1.6580 30CrNiMo8 30CrNiMo8 4340

Chemical Composition (in weight %)

C Si Mn Cr Mo Ni V W Others
0.30 max. 0.40 0.45 2.00 0.40 1.90 - - -

Description
VCNMO200 is a heat treatable, low alloy steel containing nickel, chromium and molybdenum. It is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength. 

Applications
For permanently stressed components with large cross sections for automotive and mechanical engineering. For economic performance under severe dynamic stress, parts must be designed for optimum strength or toughness. 

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210 
Density [g/cm3]: 7.82

Soft Annealing
Heat to 650-700oC, cool slowly. This will produce a maximum Brinell hardness of 248.

Normalizing
Temperature: 850-880oC.

Hardening
Harden from a temperature of 830-880oC followed by oil quenching.

Tempering
Tempering temperature: 540-680oC.

Mechanical Properties in Hardening and Tempering Condition

Diameter (mm) 0.2 % proof stress (N/mm2) Tensile strength (N/mm2) Elongation (%) Reduction of area (%) Notch impact energy (J)
<16 1050 1250-1450 9 40 35
17-40 1050 1250-1450 9 40 35
41-100 900 1100-1300 10 45 40
101-160 800 1000-1200 11 50 50
161-250 700 900-1100 12 50 50

Diagram Tempering Temperature – Mechanical Properties


Click the image to enlarge the diagram.

Forging
Hot forming temperature: 1050-850oC. 

Machinability
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.

Corrosion Resistance 
This is a low alloy steel and not a corrosion resistant alloy. Protective coating should be used.

Welding 
The alloy can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.

Cold working 
The VCNMO200 alloy may be cold worked, in the annealed condition, by conventional methods and tooling. It has good ductility.

Forms manufactured: Please see the Dimensional Sales Program. 

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.